Lithium | 23 | parts per million by weight | AES_HF |
Beryllium | N1 | parts per million by weight | ES_SQ |
Beryllium | L1 | parts per million by weight | AES_HF |
Boron | 15 | parts per million by weight | ES_SQ |
Sodium | 1.5 | percent by weight | ES_SQ |
Sodium | 2.2 | percent by weight | AES_HF |
Magnesium | 1.5 | percent by weight | ES_SQ |
Magnesium | 2 | percent by weight | AES_HF |
Aluminum | 9 | percent by weight | AES_HF |
Phosphorus | L0.2 | percent by weight | ES_SQ |
Phosphorus | 0.13 | percent by weight | AES_HF |
Potassium | 0.7 | percent by weight | AES_HF |
Calcium | 3 | percent by weight | ES_SQ |
Calcium | 4.5 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | ES_SQ |
Scandium | 25 | parts per million by weight | AES_HF |
Titanium | 1 | percent by weight | ES_SQ |
Titanium | 0.85 | percent by weight | AES_HF |
Vanadium | 300 | parts per million by weight | ES_SQ |
Vanadium | 240 | parts per million by weight | AES_HF |
Chromium | 20 | parts per million by weight | ES_SQ |
Chromium | 21 | parts per million by weight | AES_HF |
Manganese | 0.15 | percent by weight | ES_SQ |
Manganese | 0.15 | percent by weight | AES_HF |
Iron | 7 | percent by weight | ES_SQ |
Iron | 7.1 | percent by weight | AES_HF |
Cobalt | 30 | parts per million by weight | ES_SQ |
Cobalt | 23 | parts per million by weight | AES_HF |
Nickel | 5 | parts per million by weight | ES_SQ |
Nickel | 6 | parts per million by weight | AES_HF |
Copper | 20 | parts per million by weight | AA_F_AZ_H2O2_P |
Copper | 30 | parts per million by weight | ES_SQ |
Copper | 20 | parts per million by weight | AES_AZ_P |
Copper | 32 | parts per million by weight | AES_HF |
Zinc | N200 | parts per million by weight | ES_SQ |
Zinc | 55 | parts per million by weight | AA_F_AZ_H2O2_P |
Zinc | 52 | parts per million by weight | AES_AZ_P |
Zinc | 85 | parts per million by weight | AES_HF |
Gallium | 22 | parts per million by weight | AES_HF |
Gallium | 20 | parts per million by weight | ES_SQ |
Germanium | N10 | parts per million by weight | ES_SQ |
Arsenic | 20 | parts per million by weight | AA_F_AZ_H2O2_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Arsenic | 20 | parts per million by weight | AES_AZ_P |
Arsenic | 21 | parts per million by weight | AES_HF |
Strontium | 500 | parts per million by weight | ES_SQ |
Strontium | 350 | parts per million by weight | AES_HF |
Yttrium | 30 | parts per million by weight | ES_SQ |
Yttrium | 24 | parts per million by weight | AES_HF |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | L4 | parts per million by weight | AES_HF |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Molybdenum | 0.66 | parts per million by weight | AES_AZ_P |
Molybdenum | L2 | parts per million by weight | AES_HF |
Silver | 0.15 | parts per million by weight | AA_F_AZ_H2O2_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Silver | 0.11 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | N20 | parts per million by weight | ES_SQ |
Cadmium | 0.2 | parts per million by weight | AA_F_AZ_H2O2_P |
Cadmium | 0.13 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | N10 | parts per million by weight | ES_SQ |
Tin | L5 | parts per million by weight | AES_HF |
Antimony | N0.67 | parts per million by weight | AES_AZ_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | L2 | parts per million by weight | AA_F_AZ_H2O2_P |
Barium | 300 | parts per million by weight | ES_SQ |
Barium | 320 | parts per million by weight | AES_HF |
Lanthanum | N50 | parts per million by weight | ES_SQ |
Lanthanum | 12 | parts per million by weight | AES_HF |
Cerium | 27 | parts per million by weight | AES_HF |
Neodymium | 19 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Tungsten | N20 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 0.004 | parts per million by weight | AA_GF_HBr |
Gold | N0.1 | parts per million by weight | AES_AZ_P |
Gold | L8 | parts per million by weight | AES_HF |
Mercury | 0.02 | parts per million by weight | AA_CV |
Lead | 7 | parts per million by weight | AES_HF |
Lead | 5 | parts per million by weight | AA_F_AZ_H2O2_P |
Lead | 10 | parts per million by weight | ES_SQ |
Lead | 5.9 | parts per million by weight | AES_AZ_P |
Bismuth | N0.67 | parts per million by weight | AES_AZ_P |
Bismuth | L1 | parts per million by weight | AA_F_AZ_H2O2_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | L4 | parts per million by weight | AES_HF |
Thorium | N100 | parts per million by weight | ES_SQ |
Uranium | L100 | parts per million by weight | AES_HF |