Field | Value |
---|---|
Lab ID | F016831 |
Field ID | 7NA042S |
Job ID | WP38 |
Sample submitter | Eppinger, Robert G., III |
Date collected | 04/30/1997 |
Date submitted | 7/3/1997 |
Project name | Wrangell-St. Elias NP |
State | AK |
Country | United States |
Latitude (WGS84) | 62.37179216 |
Longitude (WGS84) | -143.01075141 |
Original datum | (NAD27) |
Original latitude | 62.37222 |
Original longitude | -143.00861 |
Location precision | 1 second |
Sample source | unknown |
Collection method | composite |
Primary media type | sediment |
Notes on sample | sediment from standing pool of snowmelt on Nabesna mill tailings |
(click for info) | |
Geologic map unit | -143.01075141, 62.37179216 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 8 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 1.1 | percent by weight | AES_HF |
Magnesium | 0.9 | percent by weight | AES_HF |
Aluminum | 3.7 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 0.61 | percent by weight | AES_HF |
Calcium | 5.2 | percent by weight | AES_HF |
Scandium | 8 | parts per million by weight | AES_HF |
Titanium | 0.27 | percent by weight | AES_HF |
Vanadium | 70 | parts per million by weight | AES_HF |
Chromium | 50 | parts per million by weight | AES_HF |
Manganese | 0.03 | percent by weight | AES_HF |
Iron | 9.3 | percent by weight | AES_HF |
Cobalt | 8 | parts per million by weight | AES_HF |
Nickel | 12 | parts per million by weight | AES_HF |
Copper | 540 | parts per million by weight | AES_HF |
Zinc | 140 | parts per million by weight | AES_HF |
Gallium | 8 | parts per million by weight | AES_HF |
Arsenic | 430 | parts per million by weight | AES_HF |
Strontium | 250 | parts per million by weight | AES_HF |
Yttrium | 8 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 26 | parts per million by weight | AES_HF |
Silver | 44 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Barium | 200 | parts per million by weight | AES_HF |
Lanthanum | 8 | parts per million by weight | AES_HF |
Cerium | 12 | parts per million by weight | AES_HF |
Neodymium | 19 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 1900 | parts per million by weight | AES_HF |
Bismuth | 16 | parts per million by weight | AES_HF |
Thorium | <4 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 8 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 1.1 | percent by weight | AES_HF |
Magnesium | 0.9 | percent by weight | AES_HF |
Aluminum | 3.7 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 0.61 | percent by weight | AES_HF |
Calcium | 5.2 | percent by weight | AES_HF |
Scandium | 8 | parts per million by weight | AES_HF |
Titanium | 0.27 | percent by weight | AES_HF |
Vanadium | 70 | parts per million by weight | AES_HF |
Chromium | 50 | parts per million by weight | AES_HF |
Manganese | 0.03 | percent by weight | AES_HF |
Iron | 9.3 | percent by weight | AES_HF |
Cobalt | 8 | parts per million by weight | AES_HF |
Nickel | 12 | parts per million by weight | AES_HF |
Copper | 540 | parts per million by weight | AES_HF |
Zinc | 140 | parts per million by weight | AES_HF |
Gallium | 8 | parts per million by weight | AES_HF |
Arsenic | 430 | parts per million by weight | AES_HF |
Strontium | 250 | parts per million by weight | AES_HF |
Yttrium | 8 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 26 | parts per million by weight | AES_HF |
Silver | 44 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Barium | 200 | parts per million by weight | AES_HF |
Lanthanum | 8 | parts per million by weight | AES_HF |
Cerium | 12 | parts per million by weight | AES_HF |
Neodymium | 19 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 1900 | parts per million by weight | AES_HF |
Bismuth | 16 | parts per million by weight | AES_HF |
Thorium | <4 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |