Field | Value |
---|---|
Lab ID | C102589 |
Field ID | SMC515D |
Job ID | GB84 |
Sample submitter | Carlson, Robert R. |
Date submitted | 10/31/1997 |
Project name | Kuskokwim Mineral Belt MRA |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75876226 |
Longitude (WGS84) | -157.31489494 |
Original datum | (NAD27) |
Original latitude | 61.75944 |
Original longitude | -157.3125 |
Location precision | 1 second |
Sample source | mine dump/waste rock |
Collection method | single/grab |
Primary media type | soil |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -157.31489494, 61.75876226 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 102 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.12 | percent by weight | AES_HF |
Magnesium | 0.37 | percent by weight | AES_HF |
Aluminum | 5.7 | percent by weight | AES_HF |
Phosphorus | 0.15 | percent by weight | AES_HF |
Potassium | 1.5 | percent by weight | AES_HF |
Calcium | 0.17 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.34 | percent by weight | AES_HF |
Vanadium | 156 | parts per million by weight | AES_HF |
Chromium | 83 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.6 | percent by weight | AES_HF |
Cobalt | 16 | parts per million by weight | AES_HF |
Nickel | 59 | parts per million by weight | AES_HF |
Copper | 69 | parts per million by weight | AES_HF |
Zinc | 110 | parts per million by weight | AES_HF |
Gallium | 11 | parts per million by weight | AES_HF |
Arsenic | 8570 | parts per million by weight | AES_HF |
Strontium | 412 | parts per million by weight | AES_HF |
Yttrium | 13 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | 27 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Barium | 1900 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 47 | parts per million by weight | AES_HF |
Neodymium | 23 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Tungsten | 11 | parts per million by weight | NA_SC |
Gold | 0.19 | parts per million by weight | FA_DC |
Mercury | 531 | parts per million by weight | AA_CV |
Lead | 142 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 102 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.12 | percent by weight | AES_HF |
Magnesium | 0.37 | percent by weight | AES_HF |
Aluminum | 5.7 | percent by weight | AES_HF |
Phosphorus | 0.15 | percent by weight | AES_HF |
Potassium | 1.5 | percent by weight | AES_HF |
Calcium | 0.17 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.34 | percent by weight | AES_HF |
Vanadium | 156 | parts per million by weight | AES_HF |
Chromium | 83 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.6 | percent by weight | AES_HF |
Cobalt | 16 | parts per million by weight | AES_HF |
Nickel | 59 | parts per million by weight | AES_HF |
Copper | 66 | parts per million by weight | AES_AZ_P |
Copper | 69 | parts per million by weight | AES_HF |
Zinc | 110 | parts per million by weight | AES_HF |
Zinc | 74.6 | parts per million by weight | AES_AZ_P |
Gallium | 11 | parts per million by weight | AES_HF |
Arsenic | 8570 | parts per million by weight | AES_HF |
Arsenic | 4050 | parts per million by weight | AES_AZ_P |
Strontium | 412 | parts per million by weight | AES_HF |
Yttrium | 13 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Molybdenum | 1.1 | parts per million by weight | AES_AZ_P |
Silver | 0.3 | parts per million by weight | AES_AZ_P |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <0.05 | parts per million by weight | AES_AZ_P |
Cadmium | 27 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 2560 | parts per million by weight | AES_AZ_P |
Barium | 1900 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 47 | parts per million by weight | AES_HF |
Neodymium | 23 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Tungsten | 11 | parts per million by weight | NA_SC |
Gold | 0.19 | parts per million by weight | FA_DC |
Gold | <8 | parts per million by weight | AES_HF |
Gold | <0.1 | parts per million by weight | AES_AZ_P |
Mercury | 531 | parts per million by weight | AA_CV |
Lead | 142 | parts per million by weight | AES_HF |
Lead | 71 | parts per million by weight | AES_AZ_P |
Bismuth | <1 | parts per million by weight | AES_AZ_P |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |