Field | Value |
---|---|
Lab ID | C194524 |
Field ID | 99Eb705SO |
Job ID | MRP03482 |
Sample submitter | Bailey, Elizabeth A. |
Date collected | 07/08/1999 |
Date submitted | 9/11/2001 |
Project name | Hg & As |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75553 |
Longitude (WGS84) | -157.30653 |
Original datum | WGS84 |
Original latitude | 61.75553 |
Original longitude | -157.30653 |
Location precision | 1 second |
Sampling depth | 0-8 inches |
Description of location | behind and above retort, undisturbed area, 0-8 inches |
Sample source | shrub/sage/chaparral/brush covered |
Collection method | composite |
Primary media type | soil |
Sample zone | A horizon |
Sample preparation method | standard;;Samples dried at 40 degrees C |
Sieve size | -10 mesh |
(click for info) | |
Geologic map unit | -157.30653, 61.75553 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 28 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 1.48 | percent by weight | AES_HF |
Magnesium | 0.76 | percent by weight | AES_HF |
Aluminum | 6.5 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.29 | percent by weight | AES_HF |
Calcium | 0.96 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.39 | percent by weight | AES_HF |
Vanadium | 109 | parts per million by weight | AES_HF |
Chromium | 76 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 2.85 | percent by weight | AES_HF |
Cobalt | 8 | parts per million by weight | AES_HF |
Nickel | 24 | parts per million by weight | AES_HF |
Copper | 21 | parts per million by weight | AES_HF |
Zinc | 57 | parts per million by weight | AES_HF |
Gallium | 14 | parts per million by weight | AES_HF |
Arsenic | 99.2 | parts per million by weight | AA_HG_ST |
Selenium | 0.4 | parts per million by weight | AA_HG_HF |
Strontium | 145 | parts per million by weight | AES_HF |
Yttrium | 14 | parts per million by weight | AES_HF |
Niobium | 12 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 84.3 | parts per million by weight | AA_HG_ST |
Barium | 679 | parts per million by weight | AES_HF |
Lanthanum | 32 | parts per million by weight | AES_HF |
Cerium | 69 | parts per million by weight | AES_HF |
Neodymium | 28 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 6.84 | parts per million by weight | AA_CV |
Lead | 14 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | 6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_tot | 5.51 | percent by weight | CB_IRC |
C_crb | 0.01 | percent by weight | TT_HCl |
CO2 | 0.04 | percent by weight | TT_HCl |
C_org | 5.5 | percent by weight | CP |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 28 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 1.48 | percent by weight | AES_HF |
Magnesium | 0.76 | percent by weight | AES_HF |
Aluminum | 6.5 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.29 | percent by weight | AES_HF |
Calcium | 0.96 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.39 | percent by weight | AES_HF |
Vanadium | 109 | parts per million by weight | AES_HF |
Chromium | 76 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 2.85 | percent by weight | AES_HF |
Cobalt | 8 | parts per million by weight | AES_HF |
Nickel | 24 | parts per million by weight | AES_HF |
Copper | 16.7 | parts per million by weight | AES_AZ_P |
Copper | 21 | parts per million by weight | AES_HF |
Zinc | 52.1 | parts per million by weight | AES_AZ_P |
Zinc | 57 | parts per million by weight | AES_HF |
Gallium | 14 | parts per million by weight | AES_HF |
Arsenic | 99.2 | parts per million by weight | AA_HG_ST |
Arsenic | 102 | parts per million by weight | AES_AZ_P |
Arsenic | 102 | parts per million by weight | AES_HF |
Selenium | 0.4 | parts per million by weight | AA_HG_HF |
Strontium | 145 | parts per million by weight | AES_HF |
Yttrium | 14 | parts per million by weight | AES_HF |
Niobium | 12 | parts per million by weight | AES_HF |
Molybdenum | 0.7 | parts per million by weight | AES_AZ_P |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <0.08 | parts per million by weight | AES_AZ_P |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | 0.12 | parts per million by weight | AES_AZ_P |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 84.3 | parts per million by weight | AA_HG_ST |
Antimony | 94 | parts per million by weight | AES_AZ_P |
Barium | 679 | parts per million by weight | AES_HF |
Lanthanum | 32 | parts per million by weight | AES_HF |
Cerium | 69 | parts per million by weight | AES_HF |
Neodymium | 28 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | 0.2 | parts per million by weight | AES_AZ_P |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 6.84 | parts per million by weight | AA_CV |
Lead | 7 | parts per million by weight | AES_AZ_P |
Lead | 14 | parts per million by weight | AES_HF |
Bismuth | <1 | parts per million by weight | AES_AZ_P |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | 6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Carbon (carbonate) | 0.01 | percent by weight | TT_HCl |
Carbon (organic) | 5.5 | percent by weight | CP |
Carbon dioxide | 0.04 | percent by weight | TT_HCl |
Carbon (total) | 5.51 | percent by weight | CB_IRC |