Field | Value |
---|---|
Lab ID | C194527 |
Field ID | 99Eb708SO |
Job ID | MRP03482 |
Sample submitter | Bailey, Elizabeth A. |
Date collected | 07/08/1999 |
Date submitted | 9/11/2001 |
Project name | Hg & As |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75636 |
Longitude (WGS84) | -157.30714 |
Original datum | WGS84 |
Original latitude | 61.75636 |
Original longitude | -157.30714 |
Location precision | 1 second |
Sampling depth | 11-18 inches |
Description of location | below tailings area, 11-18 inches |
Sample source | shrub/sage/chaparral/brush covered |
Collection method | composite |
Primary media type | soil |
Sample preparation method | standard;;Samples dried at 40 degrees C |
Sieve size | -10 mesh |
(click for info) | |
Geologic map unit | -157.30714, 61.75636 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 208 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.09 | percent by weight | AES_HF |
Magnesium | 0.83 | percent by weight | AES_HF |
Aluminum | 5.25 | percent by weight | AES_HF |
Phosphorus | 0.12 | percent by weight | AES_HF |
Sulfur | 0.06 | percent by weight | CB_IRC |
Potassium | 1.26 | percent by weight | AES_HF |
Calcium | 0.62 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.24 | percent by weight | AES_HF |
Vanadium | 136 | parts per million by weight | AES_HF |
Chromium | 256 | parts per million by weight | AES_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Iron | 4.38 | percent by weight | AES_HF |
Cobalt | 18 | parts per million by weight | AES_HF |
Nickel | 57 | parts per million by weight | AES_HF |
Copper | 48 | parts per million by weight | AES_HF |
Zinc | 91 | parts per million by weight | AES_HF |
Gallium | 17 | parts per million by weight | AES_HF |
Arsenic | 4590 | parts per million by weight | AA_HG_ST |
Selenium | 0.5 | parts per million by weight | AA_HG_HF |
Strontium | 348 | parts per million by weight | AES_HF |
Yttrium | 12 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | 2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 1580 | parts per million by weight | AA_HG_ST |
Barium | 1290 | parts per million by weight | AES_HF |
Lanthanum | 17 | parts per million by weight | AES_HF |
Cerium | 37 | parts per million by weight | AES_HF |
Neodymium | 19 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 256 | parts per million by weight | AA_CV |
Lead | 86 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | <6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_tot | 1.04 | percent by weight | CB_IRC |
C_crb | 0.68 | percent by weight | TT_HCl |
CO2 | 2.5 | percent by weight | TT_HCl |
C_org | 0.36 | percent by weight | CP |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 208 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.09 | percent by weight | AES_HF |
Magnesium | 0.83 | percent by weight | AES_HF |
Aluminum | 5.25 | percent by weight | AES_HF |
Phosphorus | 0.12 | percent by weight | AES_HF |
Sulfur | 0.06 | percent by weight | CB_IRC |
Potassium | 1.26 | percent by weight | AES_HF |
Calcium | 0.62 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.24 | percent by weight | AES_HF |
Vanadium | 136 | parts per million by weight | AES_HF |
Chromium | 256 | parts per million by weight | AES_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Iron | 4.38 | percent by weight | AES_HF |
Cobalt | 18 | parts per million by weight | AES_HF |
Nickel | 57 | parts per million by weight | AES_HF |
Copper | 46.3 | parts per million by weight | AES_AZ_P |
Copper | 48 | parts per million by weight | AES_HF |
Zinc | 99.7 | parts per million by weight | AES_AZ_P |
Zinc | 91 | parts per million by weight | AES_HF |
Gallium | 17 | parts per million by weight | AES_HF |
Arsenic | 4590 | parts per million by weight | AA_HG_ST |
Arsenic | 4710 | parts per million by weight | AES_AZ_P |
Arsenic | 4410 | parts per million by weight | AES_HF |
Selenium | 0.5 | parts per million by weight | AA_HG_HF |
Strontium | 348 | parts per million by weight | AES_HF |
Yttrium | 12 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | 1 | parts per million by weight | AES_AZ_P |
Molybdenum | 2 | parts per million by weight | AES_HF |
Silver | 0.1 | parts per million by weight | AES_AZ_P |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <0.05 | parts per million by weight | AES_AZ_P |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 1580 | parts per million by weight | AA_HG_ST |
Antimony | 1540 | parts per million by weight | AES_AZ_P |
Barium | 1290 | parts per million by weight | AES_HF |
Lanthanum | 17 | parts per million by weight | AES_HF |
Cerium | 37 | parts per million by weight | AES_HF |
Neodymium | 19 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | 0.1 | parts per million by weight | AES_AZ_P |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 256 | parts per million by weight | AA_CV |
Lead | 93 | parts per million by weight | AES_AZ_P |
Lead | 86 | parts per million by weight | AES_HF |
Bismuth | <1 | parts per million by weight | AES_AZ_P |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | <6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Carbon (carbonate) | 0.68 | percent by weight | TT_HCl |
Carbon (organic) | 0.36 | percent by weight | CP |
Carbon dioxide | 2.5 | percent by weight | TT_HCl |
Carbon (total) | 1.04 | percent by weight | CB_IRC |