Field | Value |
---|---|
Lab ID | C194531 |
Field ID | 99Eb712SO |
Job ID | MRP03482 |
Sample submitter | Bailey, Elizabeth A. |
Date collected | 07/09/1999 |
Date submitted | 9/11/2001 |
Project name | Hg & As |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75575 |
Longitude (WGS84) | -157.30715 |
Original datum | WGS84 |
Original latitude | 61.75575 |
Original longitude | -157.30715 |
Location precision | 1 second |
Sampling depth | 0-3 inches |
Description of location | immediately behind retort building, 0-3 inches, liquid Hg visible, site duplicate |
Sample source | mine/mill tailings |
Collection method | composite |
Primary media type | soil |
Notes on sample | tailings |
Sample preparation method | standard;;Samples dried at 40 degrees C |
Sieve size | -10 mesh |
(click for info) | |
Geologic map unit | -157.30715, 61.75575 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 274 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.46 | percent by weight | AES_HF |
Magnesium | 0.55 | percent by weight | AES_HF |
Aluminum | 8.37 | percent by weight | AES_HF |
Phosphorus | 0.09 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 2.07 | percent by weight | AES_HF |
Calcium | 0.43 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | AES_HF |
Titanium | 0.42 | percent by weight | AES_HF |
Vanadium | 214 | parts per million by weight | AES_HF |
Chromium | 111 | parts per million by weight | AES_HF |
Manganese | 0.09 | percent by weight | AES_HF |
Iron | 4.71 | percent by weight | AES_HF |
Cobalt | 25 | parts per million by weight | AES_HF |
Nickel | 71 | parts per million by weight | AES_HF |
Copper | 81 | parts per million by weight | AES_HF |
Zinc | 161 | parts per million by weight | AES_HF |
Gallium | 21 | parts per million by weight | AES_HF |
Arsenic | 1240 | parts per million by weight | AA_HG_ST |
Selenium | 0.6 | parts per million by weight | AA_HG_HF |
Strontium | 146 | parts per million by weight | AES_HF |
Yttrium | 19 | parts per million by weight | AES_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 1870 | parts per million by weight | AA_HG_ST |
Barium | 1240 | parts per million by weight | AES_HF |
Lanthanum | 30 | parts per million by weight | AES_HF |
Cerium | 61 | parts per million by weight | AES_HF |
Neodymium | 33 | parts per million by weight | AES_HF |
Europium | 2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 987 | parts per million by weight | AA_CV |
Lead | 26 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_tot | 0.87 | percent by weight | CB_IRC |
C_crb | 0.04 | percent by weight | TT_HCl |
CO2 | 0.15 | percent by weight | TT_HCl |
C_org | 0.83 | percent by weight | CP |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 274 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.46 | percent by weight | AES_HF |
Magnesium | 0.55 | percent by weight | AES_HF |
Aluminum | 8.37 | percent by weight | AES_HF |
Phosphorus | 0.09 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 2.07 | percent by weight | AES_HF |
Calcium | 0.43 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | AES_HF |
Titanium | 0.42 | percent by weight | AES_HF |
Vanadium | 214 | parts per million by weight | AES_HF |
Chromium | 111 | parts per million by weight | AES_HF |
Manganese | 0.09 | percent by weight | AES_HF |
Iron | 4.71 | percent by weight | AES_HF |
Cobalt | 25 | parts per million by weight | AES_HF |
Nickel | 71 | parts per million by weight | AES_HF |
Copper | 77.8 | parts per million by weight | AES_AZ_P |
Copper | 81 | parts per million by weight | AES_HF |
Zinc | 172 | parts per million by weight | AES_AZ_P |
Zinc | 161 | parts per million by weight | AES_HF |
Gallium | 21 | parts per million by weight | AES_HF |
Arsenic | 1240 | parts per million by weight | AA_HG_ST |
Arsenic | 1350 | parts per million by weight | AES_AZ_P |
Arsenic | 1240 | parts per million by weight | AES_HF |
Selenium | 0.6 | parts per million by weight | AA_HG_HF |
Strontium | 146 | parts per million by weight | AES_HF |
Yttrium | 19 | parts per million by weight | AES_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Molybdenum | 2.3 | parts per million by weight | AES_AZ_P |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | 0.2 | parts per million by weight | AES_AZ_P |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <0.05 | parts per million by weight | AES_AZ_P |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 1870 | parts per million by weight | AA_HG_ST |
Antimony | 2180 | parts per million by weight | AES_AZ_P |
Barium | 1240 | parts per million by weight | AES_HF |
Lanthanum | 30 | parts per million by weight | AES_HF |
Cerium | 61 | parts per million by weight | AES_HF |
Neodymium | 33 | parts per million by weight | AES_HF |
Europium | 2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <0.1 | parts per million by weight | AES_AZ_P |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 987 | parts per million by weight | AA_CV |
Lead | 22 | parts per million by weight | AES_AZ_P |
Lead | 26 | parts per million by weight | AES_HF |
Bismuth | <1 | parts per million by weight | AES_AZ_P |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Carbon (carbonate) | 0.04 | percent by weight | TT_HCl |
Carbon (organic) | 0.83 | percent by weight | CP |
Carbon dioxide | 0.15 | percent by weight | TT_HCl |
Carbon (total) | 0.87 | percent by weight | CB_IRC |