Field | Value |
---|---|
Lab ID | D305233 |
Field ID | TC71 |
Job ID | ST80 |
Sample submitter | Crock, James G., and Coel, Rebecca J. |
Date submitted | 5/16/1988 |
Project name | Geochem of Pathfinder Elements |
State | AK |
Country | United States |
Latitude (WGS84) | 64.99956909 |
Longitude (WGS84) | -147.5024704 |
Original datum | (NAD27) |
Original latitude | 65 |
Original longitude | -147.5 |
Location precision | 7.5 minutes |
Primary media type | soil |
Notes on sample | core, +10; |
Sample zone | mixture of horizons |
Soil horizon | poorly defined |
Sieve size | +10 mesh |
(click for info) | |
Geologic map unit | -147.5024704, 64.99956909 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 17 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.2 | percent by weight | AES_HF |
Magnesium | 0.36 | percent by weight | AES_HF |
Aluminum | 3.6 | percent by weight | AES_HF |
Phosphorus | 0.02 | percent by weight | AES_HF |
Potassium | 1 | percent by weight | AES_HF |
Calcium | 0.1 | percent by weight | AES_HF |
Scandium | 7 | parts per million by weight | AES_HF |
Titanium | 0.13 | percent by weight | AES_HF |
Vanadium | 53 | parts per million by weight | AES_HF |
Chromium | 47 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 2.7 | percent by weight | AES_HF |
Cobalt | 8 | parts per million by weight | AES_HF |
Nickel | 18 | parts per million by weight | AES_HF |
Copper | 20 | parts per million by weight | AES_HF |
Zinc | 43 | parts per million by weight | AES_HF |
Gallium | 10 | parts per million by weight | AES_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Strontium | 41 | parts per million by weight | AES_HF |
Yttrium | 7 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 270 | parts per million by weight | AES_HF |
Lanthanum | 18 | parts per million by weight | AES_HF |
Cerium | 34 | parts per million by weight | AES_HF |
Neodymium | 17 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | 0.1 | parts per million by weight | AA_GF_HBr |
Lead | 10 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 17 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.2 | percent by weight | AES_HF |
Magnesium | 0.36 | percent by weight | AES_HF |
Aluminum | 3.6 | percent by weight | AES_HF |
Phosphorus | 0.02 | percent by weight | AES_HF |
Potassium | 1 | percent by weight | AES_HF |
Calcium | 0.1 | percent by weight | AES_HF |
Scandium | 7 | parts per million by weight | AES_HF |
Titanium | 0.13 | percent by weight | AES_HF |
Vanadium | 53 | parts per million by weight | AES_HF |
Chromium | 47 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 2.7 | percent by weight | AES_HF |
Cobalt | 8 | parts per million by weight | AES_HF |
Nickel | 18 | parts per million by weight | AES_HF |
Copper | 20 | parts per million by weight | AES_HF |
Zinc | 43 | parts per million by weight | AES_HF |
Gallium | 10 | parts per million by weight | AES_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Strontium | 41 | parts per million by weight | AES_HF |
Yttrium | 7 | parts per million by weight | AES_HF |
Niobium | L4 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Barium | 270 | parts per million by weight | AES_HF |
Lanthanum | 18 | parts per million by weight | AES_HF |
Cerium | 34 | parts per million by weight | AES_HF |
Neodymium | 17 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | L1 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | 0.1 | parts per million by weight | AA_GF_HBr |
Lead | 10 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |