Field | Value |
---|---|
Lab ID | D310238 |
Field ID | LC88-4-4-18 |
Job ID | SX25 |
Sample submitter | Crock, James G., and Coel, Rebecca J. |
Date submitted | 8/3/1988 |
Project name | Geochem of Pathfinder Elements |
State | AK |
Country | United States |
Latitude (WGS84) | 65.51623292 |
Longitude (WGS84) | -148.55254579 |
Original datum | (NAD27) |
Original latitude | 65.51666667 |
Original longitude | -148.55 |
Location precision | 1 minute |
Sampling depth | 4-18 inches |
Primary media type | soil |
Notes on sample | horizon 4-18""; |
Sample zone | C horizon |
Soil horizon | poorly defined |
(click for info) | |
Geologic map unit | -148.55254579, 65.51623292 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 53 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.14 | percent by weight | AES_HF |
Magnesium | 0.86 | percent by weight | AES_HF |
Aluminum | 6.9 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.9 | percent by weight | AES_HF |
Calcium | 0.24 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | AES_HF |
Titanium | 0.3 | percent by weight | AES_HF |
Vanadium | 330 | parts per million by weight | AES_HF |
Chromium | 280 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 5.7 | percent by weight | AES_HF |
Cobalt | 32 | parts per million by weight | AES_HF |
Nickel | 230 | parts per million by weight | AES_HF |
Copper | 77 | parts per million by weight | AES_HF |
Zinc | 610 | parts per million by weight | AES_HF |
Gallium | 17 | parts per million by weight | AES_HF |
Arsenic | 67 | parts per million by weight | AA_HG_HF |
Strontium | 94 | parts per million by weight | AES_HF |
Yttrium | 16 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | 7 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | 4 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1600 | parts per million by weight | AES_HF |
Lanthanum | 31 | parts per million by weight | AES_HF |
Cerium | 53 | parts per million by weight | AES_HF |
Neodymium | 29 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | 0.008 | parts per million by weight | AA_GF_HBr |
Lead | 17 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 11 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_tot | 0.45 | percent by weight | CB_IRC |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 53 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.14 | percent by weight | AES_HF |
Magnesium | 0.86 | percent by weight | AES_HF |
Aluminum | 6.9 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Sulfur | L0.05 | percent by weight | CB_IRC |
Potassium | 1.9 | percent by weight | AES_HF |
Calcium | 0.24 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | AES_HF |
Titanium | 0.3 | percent by weight | AES_HF |
Vanadium | 330 | parts per million by weight | AES_HF |
Chromium | 280 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 5.7 | percent by weight | AES_HF |
Cobalt | 32 | parts per million by weight | AES_HF |
Nickel | 230 | parts per million by weight | AES_HF |
Copper | 77 | parts per million by weight | AES_HF |
Zinc | 610 | parts per million by weight | AES_HF |
Gallium | 17 | parts per million by weight | AES_HF |
Arsenic | 67 | parts per million by weight | AA_HG_HF |
Arsenic | 60 | parts per million by weight | AES_HF |
Strontium | 94 | parts per million by weight | AES_HF |
Yttrium | 16 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | 7 | parts per million by weight | AES_HF |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 4 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Barium | 1600 | parts per million by weight | AES_HF |
Lanthanum | 31 | parts per million by weight | AES_HF |
Cerium | 53 | parts per million by weight | AES_HF |
Neodymium | 29 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | 0.008 | parts per million by weight | AA_GF_HBr |
Gold | L8 | parts per million by weight | AES_HF |
Lead | 17 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 11 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |
Carbon (total) | 0.45 | percent by weight | CB_IRC |