Field | Value |
---|---|
Lab ID | D310245 |
Field ID | LC88-1-4-10 |
Job ID | SX25 |
Sample submitter | Crock, James G., and Coel, Rebecca J. |
Date submitted | 8/3/1988 |
Project name | Geochem of Pathfinder Elements |
State | AK |
Country | United States |
Latitude (WGS84) | 65.51623292 |
Longitude (WGS84) | -148.55254579 |
Original datum | (NAD27) |
Original latitude | 65.51666667 |
Original longitude | -148.55 |
Location precision | 1 minute |
Sampling depth | 4-10 inches |
Primary media type | soil |
Notes on sample | horizon 4-10""; |
Sample zone | A horizon |
Soil horizon | poorly defined |
(click for info) | |
Geologic map unit | -148.55254579, 65.51623292 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 35 | parts per million by weight | AES_HF |
Beryllium | 3 | parts per million by weight | AES_HF |
Sodium | 1 | percent by weight | AES_HF |
Magnesium | 2.1 | percent by weight | AES_HF |
Aluminum | 6.1 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Sulfur | 0.06 | percent by weight | CB_IRC |
Potassium | 1.7 | percent by weight | AES_HF |
Calcium | 0.74 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.25 | percent by weight | AES_HF |
Vanadium | 140 | parts per million by weight | AES_HF |
Chromium | 330 | parts per million by weight | AES_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Iron | 4.2 | percent by weight | AES_HF |
Cobalt | 22 | parts per million by weight | AES_HF |
Nickel | 190 | parts per million by weight | AES_HF |
Copper | 30 | parts per million by weight | AES_HF |
Zinc | 110 | parts per million by weight | AES_HF |
Gallium | 19 | parts per million by weight | AES_HF |
Arsenic | 1300 | parts per million by weight | AA_HG_HF |
Strontium | 160 | parts per million by weight | AES_HF |
Yttrium | 18 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1300 | parts per million by weight | AES_HF |
Lanthanum | 41 | parts per million by weight | AES_HF |
Cerium | 71 | parts per million by weight | AES_HF |
Neodymium | 33 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | 0.04 | parts per million by weight | AA_GF_HBr |
Lead | 18 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 12 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_tot | 1.98 | percent by weight | CB_IRC |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 35 | parts per million by weight | AES_HF |
Beryllium | 3 | parts per million by weight | AES_HF |
Sodium | 1 | percent by weight | AES_HF |
Magnesium | 2.1 | percent by weight | AES_HF |
Aluminum | 6.1 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Sulfur | 0.06 | percent by weight | CB_IRC |
Potassium | 1.7 | percent by weight | AES_HF |
Calcium | 0.74 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.25 | percent by weight | AES_HF |
Vanadium | 140 | parts per million by weight | AES_HF |
Chromium | 330 | parts per million by weight | AES_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Iron | 4.2 | percent by weight | AES_HF |
Cobalt | 22 | parts per million by weight | AES_HF |
Nickel | 190 | parts per million by weight | AES_HF |
Copper | 30 | parts per million by weight | AES_HF |
Zinc | 110 | parts per million by weight | AES_HF |
Gallium | 19 | parts per million by weight | AES_HF |
Arsenic | 1300 | parts per million by weight | AA_HG_HF |
Arsenic | 1100 | parts per million by weight | AES_HF |
Strontium | 160 | parts per million by weight | AES_HF |
Yttrium | 18 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Barium | 1300 | parts per million by weight | AES_HF |
Lanthanum | 41 | parts per million by weight | AES_HF |
Cerium | 71 | parts per million by weight | AES_HF |
Neodymium | 33 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | 0.04 | parts per million by weight | AA_GF_HBr |
Gold | L8 | parts per million by weight | AES_HF |
Lead | 18 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 12 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |
Carbon (total) | 1.98 | percent by weight | CB_IRC |