| Field | Value |
|---|---|
| Lab ID | D360707 |
| Field ID | LK108FBE |
| Job ID | UC58 |
| Sample submitter | Kelley, Karen D. |
| Date submitted | 8/27/1990 |
| Project name | Lik Soil Study |
| State | AK |
| Country | United States |
| Latitude (WGS84) | 68.16604866 |
| Longitude (WGS84) | -163.20314734 |
| Original datum | (NAD27) |
| Original latitude | 68.16666666 |
| Original longitude | -163.2 |
| Location precision | 1 minute |
| Primary media type | soil |
| Notes on sample | frost boil samples |
| Sieve size | -230 mesh |
| (click for info) | |
| Geologic map unit | -163.20314734, 68.16604866 |
| Nearby scientific data | Find additional scientific data near this location |
| Element | Measured value | Units of measure | Analytical method |
|---|---|---|---|
| Lithium | 36 | parts per million by weight | AES_HF |
| Beryllium | 2 | parts per million by weight | AES_HF |
| Sodium | 0.44 | percent by weight | AES_HF |
| Magnesium | 0.43 | percent by weight | AES_HF |
| Aluminum | 4.66 | percent by weight | AES_HF |
| Phosphorus | 0.08 | percent by weight | AES_HF |
| Potassium | 0.98 | percent by weight | AES_HF |
| Calcium | 0.2 | percent by weight | AES_HF |
| Scandium | 12 | parts per million by weight | AES_HF |
| Titanium | 0.29 | percent by weight | AES_HF |
| Vanadium | 171 | parts per million by weight | AES_HF |
| Chromium | 221 | parts per million by weight | AES_HF |
| Manganese | 0.01 | percent by weight | AES_HF |
| Iron | 6.89 | percent by weight | AES_HF |
| Cobalt | 6 | parts per million by weight | AES_HF |
| Nickel | 42 | parts per million by weight | AES_HF |
| Copper | 77 | parts per million by weight | AES_HF |
| Zinc | 725 | parts per million by weight | AES_HF |
| Gallium | 11 | parts per million by weight | AES_HF |
| Arsenic | 10 | parts per million by weight | AES_HF |
| Strontium | 104 | parts per million by weight | AES_HF |
| Yttrium | 27 | parts per million by weight | AES_HF |
| Niobium | 6 | parts per million by weight | AES_HF |
| Molybdenum | 8 | parts per million by weight | AES_HF |
| Silver | <2 | parts per million by weight | AES_HF |
| Cadmium | <2 | parts per million by weight | AES_HF |
| Tin | <10 | parts per million by weight | AES_HF |
| Barium | 916 | parts per million by weight | AES_HF |
| Lanthanum | 27 | parts per million by weight | AES_HF |
| Cerium | 47 | parts per million by weight | AES_HF |
| Neodymium | 28 | parts per million by weight | AES_HF |
| Europium | <2 | parts per million by weight | AES_HF |
| Holmium | <4 | parts per million by weight | AES_HF |
| Ytterbium | 3 | parts per million by weight | AES_HF |
| Tantalum | <40 | parts per million by weight | AES_HF |
| Gold | <8 | parts per million by weight | AES_HF |
| Lead | 90 | parts per million by weight | AES_HF |
| Bismuth | <10 | parts per million by weight | AES_HF |
| Thorium | 9 | parts per million by weight | AES_HF |
| Uranium | <100 | parts per million by weight | AES_HF |
| Element | Value | Units | Technique |
|---|---|---|---|
| Lithium | 36 | parts per million by weight | AES_HF |
| Beryllium | 2 | parts per million by weight | AES_HF |
| Sodium | 0.44 | percent by weight | AES_HF |
| Magnesium | 0.43 | percent by weight | AES_HF |
| Aluminum | 4.66 | percent by weight | AES_HF |
| Phosphorus | 0.08 | percent by weight | AES_HF |
| Potassium | 0.98 | percent by weight | AES_HF |
| Calcium | 0.2 | percent by weight | AES_HF |
| Scandium | 12 | parts per million by weight | AES_HF |
| Titanium | 0.29 | percent by weight | AES_HF |
| Vanadium | 171 | parts per million by weight | AES_HF |
| Chromium | 221 | parts per million by weight | AES_HF |
| Manganese | 0.01 | percent by weight | AES_HF |
| Iron | 6.89 | percent by weight | AES_HF |
| Cobalt | 6 | parts per million by weight | AES_HF |
| Nickel | 42 | parts per million by weight | AES_HF |
| Copper | 77 | parts per million by weight | AES_HF |
| Copper | 72 | parts per million by weight | AES_AZ_P |
| Zinc | 725 | parts per million by weight | AES_HF |
| Zinc | 550 | parts per million by weight | AES_AZ_P |
| Gallium | 11 | parts per million by weight | AES_HF |
| Arsenic | 10 | parts per million by weight | AES_HF |
| Arsenic | 10 | parts per million by weight | AES_AZ_P |
| Strontium | 104 | parts per million by weight | AES_HF |
| Yttrium | 27 | parts per million by weight | AES_HF |
| Niobium | 6 | parts per million by weight | AES_HF |
| Molybdenum | 8 | parts per million by weight | AES_HF |
| Molybdenum | 7 | parts per million by weight | AES_AZ_P |
| Silver | L2 | parts per million by weight | AES_HF |
| Silver | 1 | parts per million by weight | AES_AZ_P |
| Cadmium | L2 | parts per million by weight | AES_HF |
| Cadmium | 1.1 | parts per million by weight | AES_AZ_P |
| Tin | L10 | parts per million by weight | AES_HF |
| Antimony | 0.82 | parts per million by weight | AES_AZ_P |
| Barium | 916 | parts per million by weight | AES_HF |
| Lanthanum | 27 | parts per million by weight | AES_HF |
| Cerium | 47 | parts per million by weight | AES_HF |
| Neodymium | 28 | parts per million by weight | AES_HF |
| Europium | L2 | parts per million by weight | AES_HF |
| Holmium | L4 | parts per million by weight | AES_HF |
| Ytterbium | 3 | parts per million by weight | AES_HF |
| Tantalum | L40 | parts per million by weight | AES_HF |
| Gold | L8 | parts per million by weight | AES_HF |
| Gold | N0.15 | parts per million by weight | AES_AZ_P |
| Lead | 90 | parts per million by weight | AES_HF |
| Lead | 110 | parts per million by weight | AES_AZ_P |
| Bismuth | L10 | parts per million by weight | AES_HF |
| Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
| Thorium | 9 | parts per million by weight | AES_HF |
| Uranium | L100 | parts per million by weight | AES_HF |