Field | Value |
---|---|
Lab ID | D360715 |
Field ID | LK111FBA |
Job ID | UC59 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16604866 |
Longitude (WGS84) | -163.20314734 |
Original datum | (NAD27) |
Original latitude | 68.16666666 |
Original longitude | -163.2 |
Location precision | 1 minute |
Primary media type | soil |
Notes on sample | frost boil samples |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -163.20314734, 68.16604866 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 48 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.76 | percent by weight | AES_HF |
Magnesium | 0.79 | percent by weight | AES_HF |
Aluminum | 5.64 | percent by weight | AES_HF |
Phosphorus | 0.05 | percent by weight | AES_HF |
Potassium | 1.11 | percent by weight | AES_HF |
Calcium | 0.11 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.39 | percent by weight | AES_HF |
Vanadium | 134 | parts per million by weight | AES_HF |
Chromium | 118 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 3.54 | percent by weight | AES_HF |
Cobalt | 13 | parts per million by weight | AES_HF |
Nickel | 48 | parts per million by weight | AES_HF |
Copper | 23 | parts per million by weight | AES_HF |
Zinc | 308 | parts per million by weight | AES_HF |
Gallium | 12 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 73 | parts per million by weight | AES_HF |
Yttrium | 16 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 930 | parts per million by weight | AES_HF |
Lanthanum | 26 | parts per million by weight | AES_HF |
Cerium | 52 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 117 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 48 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.76 | percent by weight | AES_HF |
Magnesium | 0.79 | percent by weight | AES_HF |
Aluminum | 5.64 | percent by weight | AES_HF |
Phosphorus | 0.05 | percent by weight | AES_HF |
Potassium | 1.11 | percent by weight | AES_HF |
Calcium | 0.11 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.39 | percent by weight | AES_HF |
Vanadium | 134 | parts per million by weight | AES_HF |
Chromium | 118 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 3.54 | percent by weight | AES_HF |
Cobalt | 13 | parts per million by weight | AES_HF |
Nickel | 48 | parts per million by weight | AES_HF |
Copper | 23 | parts per million by weight | AES_HF |
Copper | 18 | parts per million by weight | AES_AZ_P |
Zinc | 308 | parts per million by weight | AES_HF |
Zinc | 220 | parts per million by weight | AES_AZ_P |
Gallium | 12 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Arsenic | 3.4 | parts per million by weight | AES_AZ_P |
Strontium | 73 | parts per million by weight | AES_HF |
Yttrium | 16 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 2.4 | parts per million by weight | AES_AZ_P |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 0.23 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.46 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 1.3 | parts per million by weight | AES_AZ_P |
Barium | 930 | parts per million by weight | AES_HF |
Lanthanum | 26 | parts per million by weight | AES_HF |
Cerium | 52 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 117 | parts per million by weight | AES_HF |
Lead | 130 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |