Field | Value |
---|---|
Lab ID | D360716 |
Field ID | LK112FBA |
Job ID | UC59 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16604866 |
Longitude (WGS84) | -163.20314734 |
Original datum | (NAD27) |
Original latitude | 68.16666666 |
Original longitude | -163.2 |
Location precision | 1 minute |
Primary media type | soil |
Notes on sample | frost boil samples |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -163.20314734, 68.16604866 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 53 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.77 | percent by weight | AES_HF |
Magnesium | 0.8 | percent by weight | AES_HF |
Aluminum | 6.41 | percent by weight | AES_HF |
Phosphorus | 0.06 | percent by weight | AES_HF |
Potassium | 1.25 | percent by weight | AES_HF |
Calcium | 0.16 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.41 | percent by weight | AES_HF |
Vanadium | 147 | parts per million by weight | AES_HF |
Chromium | 127 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 4.56 | percent by weight | AES_HF |
Cobalt | 13 | parts per million by weight | AES_HF |
Nickel | 47 | parts per million by weight | AES_HF |
Copper | 27 | parts per million by weight | AES_HF |
Zinc | 422 | parts per million by weight | AES_HF |
Gallium | 14 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 91 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1010 | parts per million by weight | AES_HF |
Lanthanum | 29 | parts per million by weight | AES_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Neodymium | 25 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 629 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 53 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.77 | percent by weight | AES_HF |
Magnesium | 0.8 | percent by weight | AES_HF |
Aluminum | 6.41 | percent by weight | AES_HF |
Phosphorus | 0.06 | percent by weight | AES_HF |
Potassium | 1.25 | percent by weight | AES_HF |
Calcium | 0.16 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.41 | percent by weight | AES_HF |
Vanadium | 147 | parts per million by weight | AES_HF |
Chromium | 127 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 4.56 | percent by weight | AES_HF |
Cobalt | 13 | parts per million by weight | AES_HF |
Nickel | 47 | parts per million by weight | AES_HF |
Copper | 27 | parts per million by weight | AES_HF |
Copper | 23 | parts per million by weight | AES_AZ_P |
Zinc | 422 | parts per million by weight | AES_HF |
Zinc | 330 | parts per million by weight | AES_AZ_P |
Gallium | 14 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Arsenic | 3.5 | parts per million by weight | AES_AZ_P |
Strontium | 91 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Molybdenum | 3.3 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 0.3 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.36 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 2.5 | parts per million by weight | AES_AZ_P |
Barium | 1010 | parts per million by weight | AES_HF |
Lanthanum | 29 | parts per million by weight | AES_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Neodymium | 25 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 800 | parts per million by weight | AES_AZ_P |
Lead | 629 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |