Field | Value |
---|---|
Lab ID | D360847 |
Field ID | LK014SB |
Job ID | UC66 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.1696622 |
Longitude (WGS84) | -163.19842777 |
Original datum | (NAD27) |
Original latitude | 68.17028 |
Original longitude | -163.19528 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -30 +80 mesh |
(click for info) | |
Geologic map unit | -163.19842777, 68.1696622 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 43 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.58 | percent by weight | AES_HF |
Magnesium | 0.68 | percent by weight | AES_HF |
Aluminum | 6.37 | percent by weight | AES_HF |
Phosphorus | 0.2 | percent by weight | AES_HF |
Potassium | 1.54 | percent by weight | AES_HF |
Calcium | 0.12 | percent by weight | AES_HF |
Scandium | 15 | parts per million by weight | AES_HF |
Titanium | 0.34 | percent by weight | AES_HF |
Vanadium | 353 | parts per million by weight | AES_HF |
Chromium | 130 | parts per million by weight | AES_HF |
Manganese | 0.14 | percent by weight | AES_HF |
Iron | 4.7 | percent by weight | AES_HF |
Cobalt | 24 | parts per million by weight | AES_HF |
Nickel | 45 | parts per million by weight | AES_HF |
Copper | 115 | parts per million by weight | AES_HF |
Zinc | 223 | parts per million by weight | AES_HF |
Gallium | 16 | parts per million by weight | AES_HF |
Arsenic | 30 | parts per million by weight | AES_HF |
Strontium | 206 | parts per million by weight | AES_HF |
Yttrium | 21 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 13 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 2710 | parts per million by weight | AES_HF |
Lanthanum | 31 | parts per million by weight | AES_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Neodymium | 28 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 64 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 10 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 43 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.58 | percent by weight | AES_HF |
Magnesium | 0.68 | percent by weight | AES_HF |
Aluminum | 6.37 | percent by weight | AES_HF |
Phosphorus | 0.2 | percent by weight | AES_HF |
Potassium | 1.54 | percent by weight | AES_HF |
Calcium | 0.12 | percent by weight | AES_HF |
Scandium | 15 | parts per million by weight | AES_HF |
Titanium | 0.34 | percent by weight | AES_HF |
Vanadium | 353 | parts per million by weight | AES_HF |
Chromium | 130 | parts per million by weight | AES_HF |
Manganese | 0.14 | percent by weight | AES_HF |
Iron | 4.7 | percent by weight | AES_HF |
Cobalt | 24 | parts per million by weight | AES_HF |
Nickel | 45 | parts per million by weight | AES_HF |
Copper | 115 | parts per million by weight | AES_HF |
Copper | 110 | parts per million by weight | AES_AZ_P |
Zinc | 170 | parts per million by weight | AES_AZ_P |
Zinc | 223 | parts per million by weight | AES_HF |
Gallium | 16 | parts per million by weight | AES_HF |
Arsenic | 30 | parts per million by weight | AES_HF |
Arsenic | 18 | parts per million by weight | AES_AZ_P |
Strontium | 206 | parts per million by weight | AES_HF |
Yttrium | 21 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 13 | parts per million by weight | AES_HF |
Molybdenum | 14 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 1.7 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.64 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 4.3 | parts per million by weight | AES_AZ_P |
Barium | 2710 | parts per million by weight | AES_HF |
Lanthanum | 31 | parts per million by weight | AES_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Neodymium | 28 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 64 | parts per million by weight | AES_HF |
Lead | 70 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 10 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |