Field | Value |
---|---|
Lab ID | D360929 |
Field ID | LK103SB |
Job ID | UC68 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.17660284 |
Longitude (WGS84) | -163.1759284 |
Original datum | (NAD27) |
Original latitude | 68.17722 |
Original longitude | -163.17278 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -30 +80 mesh |
(click for info) | |
Geologic map unit | -163.1759284, 68.17660284 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 47 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.1 | percent by weight | AES_HF |
Magnesium | 0.18 | percent by weight | AES_HF |
Aluminum | 5.33 | percent by weight | AES_HF |
Phosphorus | 0.09 | percent by weight | AES_HF |
Potassium | 1.1 | percent by weight | AES_HF |
Calcium | 0.47 | percent by weight | AES_HF |
Scandium | 12 | parts per million by weight | AES_HF |
Titanium | 0.21 | percent by weight | AES_HF |
Vanadium | 161 | parts per million by weight | AES_HF |
Chromium | 216 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.53 | percent by weight | AES_HF |
Cobalt | 25 | parts per million by weight | AES_HF |
Nickel | 186 | parts per million by weight | AES_HF |
Copper | 61 | parts per million by weight | AES_HF |
Zinc | 536 | parts per million by weight | AES_HF |
Gallium | 11 | parts per million by weight | AES_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Strontium | 78 | parts per million by weight | AES_HF |
Yttrium | 38 | parts per million by weight | AES_HF |
Niobium | 5 | parts per million by weight | AES_HF |
Molybdenum | 8 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 565 | parts per million by weight | AES_HF |
Lanthanum | 32 | parts per million by weight | AES_HF |
Cerium | 45 | parts per million by weight | AES_HF |
Neodymium | 25 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 19 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 47 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.1 | percent by weight | AES_HF |
Magnesium | 0.18 | percent by weight | AES_HF |
Aluminum | 5.33 | percent by weight | AES_HF |
Phosphorus | 0.09 | percent by weight | AES_HF |
Potassium | 1.1 | percent by weight | AES_HF |
Calcium | 0.47 | percent by weight | AES_HF |
Scandium | 12 | parts per million by weight | AES_HF |
Titanium | 0.21 | percent by weight | AES_HF |
Vanadium | 161 | parts per million by weight | AES_HF |
Chromium | 216 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.53 | percent by weight | AES_HF |
Cobalt | 25 | parts per million by weight | AES_HF |
Nickel | 186 | parts per million by weight | AES_HF |
Copper | 61 | parts per million by weight | AES_HF |
Copper | 54 | parts per million by weight | AES_AZ_P |
Zinc | 536 | parts per million by weight | AES_HF |
Zinc | 390 | parts per million by weight | AES_AZ_P |
Gallium | 11 | parts per million by weight | AES_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Arsenic | 28 | parts per million by weight | AES_AZ_P |
Strontium | 78 | parts per million by weight | AES_HF |
Yttrium | 38 | parts per million by weight | AES_HF |
Niobium | 5 | parts per million by weight | AES_HF |
Molybdenum | 8 | parts per million by weight | AES_HF |
Molybdenum | 8.1 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 1.5 | parts per million by weight | AES_AZ_P |
Cadmium | 1.5 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | N0.6 | parts per million by weight | AES_AZ_P |
Barium | 565 | parts per million by weight | AES_HF |
Lanthanum | 32 | parts per million by weight | AES_HF |
Cerium | 45 | parts per million by weight | AES_HF |
Neodymium | 25 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 19 | parts per million by weight | AES_HF |
Lead | 22 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |