Field | Value |
---|---|
Lab ID | D360973 |
Field ID | LK037SE |
Job ID | UC69 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16994204 |
Longitude (WGS84) | -163.20703793 |
Original datum | (NAD27) |
Original latitude | 68.17056 |
Original longitude | -163.20389 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -230 mesh |
(click for info) | |
Geologic map unit | -163.20703793, 68.16994204 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 46 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.77 | percent by weight | AES_HF |
Magnesium | 0.95 | percent by weight | AES_HF |
Aluminum | 7.31 | percent by weight | AES_HF |
Phosphorus | 0.06 | percent by weight | AES_HF |
Potassium | 1.91 | percent by weight | AES_HF |
Calcium | 0.66 | percent by weight | AES_HF |
Scandium | 18 | parts per million by weight | AES_HF |
Titanium | 0.42 | percent by weight | AES_HF |
Vanadium | 161 | parts per million by weight | AES_HF |
Chromium | 150 | parts per million by weight | AES_HF |
Manganese | 0.09 | percent by weight | AES_HF |
Iron | 4.63 | percent by weight | AES_HF |
Cobalt | 20 | parts per million by weight | AES_HF |
Nickel | 60 | parts per million by weight | AES_HF |
Copper | 40 | parts per million by weight | AES_HF |
Zinc | 122 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 20 | parts per million by weight | AES_HF |
Strontium | 81 | parts per million by weight | AES_HF |
Yttrium | 36 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | 4 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 945 | parts per million by weight | AES_HF |
Lanthanum | 37 | parts per million by weight | AES_HF |
Cerium | 68 | parts per million by weight | AES_HF |
Neodymium | 39 | parts per million by weight | AES_HF |
Europium | 2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 23 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 13 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 46 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.77 | percent by weight | AES_HF |
Magnesium | 0.95 | percent by weight | AES_HF |
Aluminum | 7.31 | percent by weight | AES_HF |
Phosphorus | 0.06 | percent by weight | AES_HF |
Potassium | 1.91 | percent by weight | AES_HF |
Calcium | 0.66 | percent by weight | AES_HF |
Scandium | 18 | parts per million by weight | AES_HF |
Titanium | 0.42 | percent by weight | AES_HF |
Vanadium | 161 | parts per million by weight | AES_HF |
Chromium | 150 | parts per million by weight | AES_HF |
Manganese | 0.09 | percent by weight | AES_HF |
Iron | 4.63 | percent by weight | AES_HF |
Cobalt | 20 | parts per million by weight | AES_HF |
Nickel | 60 | parts per million by weight | AES_HF |
Copper | 40 | parts per million by weight | AES_HF |
Copper | 36 | parts per million by weight | AES_AZ_P |
Zinc | 93 | parts per million by weight | AES_AZ_P |
Zinc | 122 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 20 | parts per million by weight | AES_HF |
Arsenic | 17 | parts per million by weight | AES_AZ_P |
Strontium | 81 | parts per million by weight | AES_HF |
Yttrium | 36 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | 4 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 0.33 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.32 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 1.1 | parts per million by weight | AES_AZ_P |
Barium | 945 | parts per million by weight | AES_HF |
Lanthanum | 37 | parts per million by weight | AES_HF |
Cerium | 68 | parts per million by weight | AES_HF |
Neodymium | 39 | parts per million by weight | AES_HF |
Europium | 2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 25 | parts per million by weight | AES_AZ_P |
Lead | 23 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 13 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |