Field | Value |
---|---|
Lab ID | D360997 |
Field ID | LK068SE |
Job ID | UC70 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16910233 |
Longitude (WGS84) | -163.19036758 |
Original datum | (NAD27) |
Original latitude | 68.16972 |
Original longitude | -163.18722 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -230 mesh |
(click for info) | |
Geologic map unit | -163.19036758, 68.16910233 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 45 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.84 | percent by weight | AES_HF |
Magnesium | 0.88 | percent by weight | AES_HF |
Aluminum | 6.52 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Potassium | 1.33 | percent by weight | AES_HF |
Calcium | 0.6 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.4 | percent by weight | AES_HF |
Vanadium | 139 | parts per million by weight | AES_HF |
Chromium | 124 | parts per million by weight | AES_HF |
Manganese | 0.02 | percent by weight | AES_HF |
Iron | 3.54 | percent by weight | AES_HF |
Cobalt | 12 | parts per million by weight | AES_HF |
Nickel | 58 | parts per million by weight | AES_HF |
Copper | 28 | parts per million by weight | AES_HF |
Zinc | 248 | parts per million by weight | AES_HF |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 91 | parts per million by weight | AES_HF |
Yttrium | 35 | parts per million by weight | AES_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1060 | parts per million by weight | AES_HF |
Lanthanum | 39 | parts per million by weight | AES_HF |
Cerium | 62 | parts per million by weight | AES_HF |
Neodymium | 34 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 24 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 45 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.84 | percent by weight | AES_HF |
Magnesium | 0.88 | percent by weight | AES_HF |
Aluminum | 6.52 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Potassium | 1.33 | percent by weight | AES_HF |
Calcium | 0.6 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.4 | percent by weight | AES_HF |
Vanadium | 139 | parts per million by weight | AES_HF |
Chromium | 124 | parts per million by weight | AES_HF |
Manganese | 0.02 | percent by weight | AES_HF |
Iron | 3.54 | percent by weight | AES_HF |
Cobalt | 12 | parts per million by weight | AES_HF |
Nickel | 58 | parts per million by weight | AES_HF |
Copper | 28 | parts per million by weight | AES_HF |
Copper | 23 | parts per million by weight | AES_AZ_P |
Zinc | 248 | parts per million by weight | AES_HF |
Zinc | 180 | parts per million by weight | AES_AZ_P |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Arsenic | 4.2 | parts per million by weight | AES_AZ_P |
Strontium | 91 | parts per million by weight | AES_HF |
Yttrium | 35 | parts per million by weight | AES_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Molybdenum | 1.1 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 0.29 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.44 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 0.76 | parts per million by weight | AES_AZ_P |
Barium | 1060 | parts per million by weight | AES_HF |
Lanthanum | 39 | parts per million by weight | AES_HF |
Cerium | 62 | parts per million by weight | AES_HF |
Neodymium | 34 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 24 | parts per million by weight | AES_HF |
Lead | 26 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |