Field | Value |
---|---|
Lab ID | D361001 |
Field ID | LK071SE |
Job ID | UC70 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16632196 |
Longitude (WGS84) | -163.20536741 |
Original datum | (NAD27) |
Original latitude | 68.16694 |
Original longitude | -163.20222 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -230 mesh |
(click for info) | |
Geologic map unit | -163.20536741, 68.16632196 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 42 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.67 | percent by weight | AES_HF |
Magnesium | 0.79 | percent by weight | AES_HF |
Aluminum | 7.7 | percent by weight | AES_HF |
Phosphorus | 0.13 | percent by weight | AES_HF |
Potassium | 1.74 | percent by weight | AES_HF |
Calcium | 0.17 | percent by weight | AES_HF |
Scandium | 17 | parts per million by weight | AES_HF |
Titanium | 0.38 | percent by weight | AES_HF |
Vanadium | 409 | parts per million by weight | AES_HF |
Chromium | 138 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 5.76 | percent by weight | AES_HF |
Cobalt | 16 | parts per million by weight | AES_HF |
Nickel | 48 | parts per million by weight | AES_HF |
Copper | 96 | parts per million by weight | AES_HF |
Zinc | 232 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Strontium | 184 | parts per million by weight | AES_HF |
Yttrium | 20 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | 18 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1610 | parts per million by weight | AES_HF |
Lanthanum | 30 | parts per million by weight | AES_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Neodymium | 29 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 51 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 42 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.67 | percent by weight | AES_HF |
Magnesium | 0.79 | percent by weight | AES_HF |
Aluminum | 7.7 | percent by weight | AES_HF |
Phosphorus | 0.13 | percent by weight | AES_HF |
Potassium | 1.74 | percent by weight | AES_HF |
Calcium | 0.17 | percent by weight | AES_HF |
Scandium | 17 | parts per million by weight | AES_HF |
Titanium | 0.38 | percent by weight | AES_HF |
Vanadium | 409 | parts per million by weight | AES_HF |
Chromium | 138 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 5.76 | percent by weight | AES_HF |
Cobalt | 16 | parts per million by weight | AES_HF |
Nickel | 48 | parts per million by weight | AES_HF |
Copper | 96 | parts per million by weight | AES_HF |
Copper | 82 | parts per million by weight | AES_AZ_P |
Zinc | 160 | parts per million by weight | AES_AZ_P |
Zinc | 232 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Arsenic | 18 | parts per million by weight | AES_AZ_P |
Strontium | 184 | parts per million by weight | AES_HF |
Yttrium | 20 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | 18 | parts per million by weight | AES_HF |
Molybdenum | 17 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 0.94 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.55 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 4.4 | parts per million by weight | AES_AZ_P |
Barium | 1610 | parts per million by weight | AES_HF |
Lanthanum | 30 | parts per million by weight | AES_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Neodymium | 29 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 3 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 51 | parts per million by weight | AES_HF |
Lead | 87 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |