Field | Value |
---|---|
Lab ID | D361052 |
Field ID | LK015SC |
Job ID | UC72 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16966219 |
Longitude (WGS84) | -163.19897778 |
Original datum | (NAD27) |
Original latitude | 68.17028 |
Original longitude | -163.19583 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -80 +230 mesh |
(click for info) | |
Geologic map unit | -163.19897778, 68.16966219 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 33 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 0.1 | percent by weight | AES_HF |
Magnesium | 0.11 | percent by weight | AES_HF |
Aluminum | 1.6 | percent by weight | AES_HF |
Phosphorus | 0.04 | percent by weight | AES_HF |
Potassium | 0.38 | percent by weight | AES_HF |
Calcium | 0.03 | percent by weight | AES_HF |
Scandium | 4 | parts per million by weight | AES_HF |
Titanium | 0.11 | percent by weight | AES_HF |
Vanadium | 117 | parts per million by weight | AES_HF |
Chromium | 56 | parts per million by weight | AES_HF |
Manganese | 0.0053 | percent by weight | AES_HF |
Iron | 3.36 | percent by weight | AES_HF |
Cobalt | 2 | parts per million by weight | AES_HF |
Nickel | 10 | parts per million by weight | AES_HF |
Copper | 42 | parts per million by weight | AES_HF |
Zinc | 73 | parts per million by weight | AES_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 64 | parts per million by weight | AES_HF |
Yttrium | 10 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 12 | parts per million by weight | AES_HF |
Silver | 4 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 108 | parts per million by weight | AES_HF |
Lanthanum | 9 | parts per million by weight | AES_HF |
Cerium | 17 | parts per million by weight | AES_HF |
Neodymium | 10 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 178 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | <4 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 33 | parts per million by weight | AES_HF |
Beryllium | L1 | parts per million by weight | AES_HF |
Sodium | 0.1 | percent by weight | AES_HF |
Magnesium | 0.11 | percent by weight | AES_HF |
Aluminum | 1.6 | percent by weight | AES_HF |
Phosphorus | 0.04 | percent by weight | AES_HF |
Potassium | 0.38 | percent by weight | AES_HF |
Calcium | 0.03 | percent by weight | AES_HF |
Scandium | 4 | parts per million by weight | AES_HF |
Titanium | 0.11 | percent by weight | AES_HF |
Vanadium | 117 | parts per million by weight | AES_HF |
Chromium | 56 | parts per million by weight | AES_HF |
Manganese | 0.0053 | percent by weight | AES_HF |
Iron | 3.36 | percent by weight | AES_HF |
Cobalt | 2 | parts per million by weight | AES_HF |
Nickel | 10 | parts per million by weight | AES_HF |
Copper | 42 | parts per million by weight | AES_HF |
Copper | 34 | parts per million by weight | AES_AZ_P |
Zinc | 73 | parts per million by weight | AES_HF |
Zinc | 55 | parts per million by weight | AES_AZ_P |
Gallium | L4 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Arsenic | 11 | parts per million by weight | AES_AZ_P |
Strontium | 64 | parts per million by weight | AES_HF |
Yttrium | 10 | parts per million by weight | AES_HF |
Niobium | L4 | parts per million by weight | AES_HF |
Molybdenum | 12 | parts per million by weight | AES_HF |
Molybdenum | 7.9 | parts per million by weight | AES_AZ_P |
Silver | 4 | parts per million by weight | AES_HF |
Silver | 2.6 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.26 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 30 | parts per million by weight | AES_AZ_P |
Barium | 108 | parts per million by weight | AES_HF |
Lanthanum | 9 | parts per million by weight | AES_HF |
Cerium | 17 | parts per million by weight | AES_HF |
Neodymium | 10 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | L1 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 178 | parts per million by weight | AES_HF |
Lead | 260 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | L4 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |