Field | Value |
---|---|
Lab ID | D361056 |
Field ID | LK019SC |
Job ID | UC72 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16632186 |
Longitude (WGS84) | -163.21064749 |
Original datum | (NAD27) |
Original latitude | 68.16694 |
Original longitude | -163.2075 |
Location precision | 1 second |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -80 +230 mesh |
(click for info) | |
Geologic map unit | -163.21064749, 68.16632186 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 105 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.36 | percent by weight | AES_HF |
Magnesium | 0.92 | percent by weight | AES_HF |
Aluminum | 9.24 | percent by weight | AES_HF |
Phosphorus | 0.06 | percent by weight | AES_HF |
Potassium | 2.07 | percent by weight | AES_HF |
Calcium | 0.89 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | AES_HF |
Titanium | 0.22 | percent by weight | AES_HF |
Vanadium | 255 | parts per million by weight | AES_HF |
Chromium | 179 | parts per million by weight | AES_HF |
Manganese | 0.02 | percent by weight | AES_HF |
Iron | 2.54 | percent by weight | AES_HF |
Cobalt | 23 | parts per million by weight | AES_HF |
Nickel | 137 | parts per million by weight | AES_HF |
Copper | 89 | parts per million by weight | AES_HF |
Zinc | 562 | parts per million by weight | AES_HF |
Gallium | 22 | parts per million by weight | AES_HF |
Arsenic | <10 | parts per million by weight | AES_HF |
Strontium | 125 | parts per million by weight | AES_HF |
Yttrium | 22 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | 4 | parts per million by weight | AES_HF |
Cadmium | 2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 294 | parts per million by weight | AES_HF |
Lanthanum | 20 | parts per million by weight | AES_HF |
Cerium | 37 | parts per million by weight | AES_HF |
Neodymium | 20 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 174 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 105 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.36 | percent by weight | AES_HF |
Magnesium | 0.92 | percent by weight | AES_HF |
Aluminum | 9.24 | percent by weight | AES_HF |
Phosphorus | 0.06 | percent by weight | AES_HF |
Potassium | 2.07 | percent by weight | AES_HF |
Calcium | 0.89 | percent by weight | AES_HF |
Scandium | 20 | parts per million by weight | AES_HF |
Titanium | 0.22 | percent by weight | AES_HF |
Vanadium | 255 | parts per million by weight | AES_HF |
Chromium | 179 | parts per million by weight | AES_HF |
Manganese | 0.02 | percent by weight | AES_HF |
Iron | 2.54 | percent by weight | AES_HF |
Cobalt | 23 | parts per million by weight | AES_HF |
Nickel | 137 | parts per million by weight | AES_HF |
Copper | 89 | parts per million by weight | AES_HF |
Copper | 77 | parts per million by weight | AES_AZ_P |
Zinc | 562 | parts per million by weight | AES_HF |
Zinc | 340 | parts per million by weight | AES_AZ_P |
Gallium | 22 | parts per million by weight | AES_HF |
Arsenic | L10 | parts per million by weight | AES_HF |
Arsenic | N0.6 | parts per million by weight | AES_AZ_P |
Strontium | 125 | parts per million by weight | AES_HF |
Yttrium | 22 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Molybdenum | 0.96 | parts per million by weight | AES_AZ_P |
Silver | 4 | parts per million by weight | AES_HF |
Silver | 3.2 | parts per million by weight | AES_AZ_P |
Cadmium | 2 | parts per million by weight | AES_HF |
Cadmium | 2.5 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 3.3 | parts per million by weight | AES_AZ_P |
Barium | 294 | parts per million by weight | AES_HF |
Lanthanum | 20 | parts per million by weight | AES_HF |
Cerium | 37 | parts per million by weight | AES_HF |
Neodymium | 20 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 174 | parts per million by weight | AES_HF |
Lead | 290 | parts per million by weight | AES_AZ_P |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |