Field | Value |
---|---|
Lab ID | D361094 |
Field ID | LK051SC |
Job ID | UC73 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16605197 |
Longitude (WGS84) | -163.20453736 |
Original datum | (NAD27) |
Original latitude | 68.16667 |
Original longitude | -163.20139 |
Location precision | 5 minutes |
Collection method | composite |
Primary media type | soil |
Notes on sample | soil samples |
Sample zone | B horizon |
Sieve size | -80 +230 mesh |
(click for info) | |
Geologic map unit | -163.20453736, 68.16605197 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 76 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.99 | percent by weight | AES_HF |
Magnesium | 1.02 | percent by weight | AES_HF |
Aluminum | 7.68 | percent by weight | AES_HF |
Phosphorus | 0.12 | percent by weight | AES_HF |
Potassium | 1.56 | percent by weight | AES_HF |
Calcium | 0.33 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.43 | percent by weight | AES_HF |
Vanadium | 188 | parts per million by weight | AES_HF |
Chromium | 134 | parts per million by weight | AES_HF |
Manganese | 0.22 | percent by weight | AES_HF |
Iron | 5.09 | percent by weight | AES_HF |
Cobalt | 41 | parts per million by weight | AES_HF |
Nickel | 57 | parts per million by weight | AES_HF |
Copper | 34 | parts per million by weight | AES_HF |
Zinc | 251 | parts per million by weight | AES_HF |
Gallium | 20 | parts per million by weight | AES_HF |
Arsenic | 20 | parts per million by weight | AES_HF |
Strontium | 95 | parts per million by weight | AES_HF |
Yttrium | 15 | parts per million by weight | AES_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Molybdenum | 7 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 2760 | parts per million by weight | AES_HF |
Lanthanum | 28 | parts per million by weight | AES_HF |
Cerium | 57 | parts per million by weight | AES_HF |
Neodymium | 27 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 40 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 10 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 76 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.99 | percent by weight | AES_HF |
Magnesium | 1.02 | percent by weight | AES_HF |
Aluminum | 7.68 | percent by weight | AES_HF |
Phosphorus | 0.12 | percent by weight | AES_HF |
Potassium | 1.56 | percent by weight | AES_HF |
Calcium | 0.33 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.43 | percent by weight | AES_HF |
Vanadium | 188 | parts per million by weight | AES_HF |
Chromium | 134 | parts per million by weight | AES_HF |
Manganese | 0.22 | percent by weight | AES_HF |
Iron | 5.09 | percent by weight | AES_HF |
Cobalt | 41 | parts per million by weight | AES_HF |
Nickel | 57 | parts per million by weight | AES_HF |
Copper | 34 | parts per million by weight | AES_HF |
Copper | 27 | parts per million by weight | AES_AZ_P |
Zinc | 251 | parts per million by weight | AES_HF |
Zinc | 150 | parts per million by weight | AES_AZ_P |
Gallium | 20 | parts per million by weight | AES_HF |
Arsenic | 20 | parts per million by weight | AES_HF |
Arsenic | 6.3 | parts per million by weight | AES_AZ_P |
Strontium | 95 | parts per million by weight | AES_HF |
Yttrium | 15 | parts per million by weight | AES_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Molybdenum | 7 | parts per million by weight | AES_HF |
Molybdenum | 4.3 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Silver | 0.07 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Cadmium | 0.46 | parts per million by weight | AES_AZ_P |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 0.86 | parts per million by weight | AES_AZ_P |
Barium | 2760 | parts per million by weight | AES_HF |
Lanthanum | 28 | parts per million by weight | AES_HF |
Cerium | 57 | parts per million by weight | AES_HF |
Neodymium | 27 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 40 | parts per million by weight | AES_HF |
Lead | 47 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 10 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |