Field | Value |
---|---|
Lab ID | D578475 |
Field ID | 94AEB036S |
Job ID | WF99 |
Sample submitter | Bailey, Elizabeth A. |
Date submitted | 2/8/1995 |
Project name | Sleetmute AMRAP |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75793335 |
Longitude (WGS84) | -157.31517266 |
Original datum | (NAD27) |
Original latitude | 61.75861111 |
Original longitude | -157.31277778 |
Location precision | 1 second |
Sample source | forest/scattered timberland |
Collection method | single/grab |
Primary media type | soil |
Notes on sample | soil; |
Sample zone | no horizons |
Sieve size | -10 mesh |
(click for info) | |
Geologic map unit | -157.31517266, 61.75793335 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 26 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 1.3 | percent by weight | AES_HF |
Magnesium | 0.71 | percent by weight | AES_HF |
Aluminum | 6 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Potassium | 1.3 | percent by weight | AES_HF |
Calcium | 0.88 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.4 | percent by weight | AES_HF |
Vanadium | 110 | parts per million by weight | AES_HF |
Chromium | 74 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 3.1 | percent by weight | AES_HF |
Cobalt | 7 | parts per million by weight | AES_HF |
Nickel | 24 | parts per million by weight | AES_HF |
Copper | 18 | parts per million by weight | AES_HF |
Zinc | 54 | parts per million by weight | AES_HF |
Gallium | 14 | parts per million by weight | AES_HF |
Arsenic | 19 | parts per million by weight | AES_HF |
Strontium | 130 | parts per million by weight | AES_HF |
Yttrium | 15 | parts per million by weight | AES_HF |
Niobium | 15 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Barium | 670 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 39 | parts per million by weight | AES_HF |
Neodymium | 18 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 0.64 | parts per million by weight | AA_CV |
Lead | 11 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 26 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 1.3 | percent by weight | AES_HF |
Magnesium | 0.71 | percent by weight | AES_HF |
Aluminum | 6 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Potassium | 1.3 | percent by weight | AES_HF |
Calcium | 0.88 | percent by weight | AES_HF |
Scandium | 11 | parts per million by weight | AES_HF |
Titanium | 0.4 | percent by weight | AES_HF |
Vanadium | 110 | parts per million by weight | AES_HF |
Chromium | 74 | parts per million by weight | AES_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Iron | 3.1 | percent by weight | AES_HF |
Cobalt | 7 | parts per million by weight | AES_HF |
Nickel | 24 | parts per million by weight | AES_HF |
Copper | 18 | parts per million by weight | AES_HF |
Zinc | 54 | parts per million by weight | AES_HF |
Gallium | 14 | parts per million by weight | AES_HF |
Arsenic | 19 | parts per million by weight | AES_HF |
Strontium | 130 | parts per million by weight | AES_HF |
Yttrium | 15 | parts per million by weight | AES_HF |
Niobium | 15 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L5 | parts per million by weight | AES_HF |
Barium | 670 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 39 | parts per million by weight | AES_HF |
Neodymium | 18 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Mercury | 0.64 | parts per million by weight | AA_CV |
Lead | 11 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |