Field | Value |
---|---|
Lab ID | D578486 |
Field ID | 94AEB011S |
Job ID | WF99 |
Sample submitter | Bailey, Elizabeth A. |
Date submitted | 2/8/1995 |
Project name | Sleetmute AMRAP |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75959998 |
Longitude (WGS84) | -157.31933952 |
Original datum | (NAD27) |
Original latitude | 61.76027778 |
Original longitude | -157.31694444 |
Location precision | 1 second |
Sample source | forest/scattered timberland |
Collection method | single/grab |
Primary media type | soil |
Notes on sample | soil; |
Sample zone | no horizons |
Sieve size | -10 mesh |
(click for info) | |
Geologic map unit | -157.31933952, 61.75959998 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 270 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.44 | percent by weight | AES_HF |
Magnesium | 0.47 | percent by weight | AES_HF |
Aluminum | 7.7 | percent by weight | AES_HF |
Phosphorus | 0.09 | percent by weight | AES_HF |
Potassium | 2.1 | percent by weight | AES_HF |
Calcium | 0.38 | percent by weight | AES_HF |
Scandium | 18 | parts per million by weight | AES_HF |
Titanium | 0.34 | percent by weight | AES_HF |
Vanadium | 200 | parts per million by weight | AES_HF |
Chromium | 130 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.6 | percent by weight | AES_HF |
Cobalt | 21 | parts per million by weight | AES_HF |
Nickel | 76 | parts per million by weight | AES_HF |
Copper | 67 | parts per million by weight | AES_HF |
Zinc | 120 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 730 | parts per million by weight | AES_HF |
Strontium | 120 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 13 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Barium | 1200 | parts per million by weight | AES_HF |
Lanthanum | 23 | parts per million by weight | AES_HF |
Cerium | 42 | parts per million by weight | AES_HF |
Neodymium | 24 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 140 | parts per million by weight | AA_CV |
Lead | 15 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 270 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.44 | percent by weight | AES_HF |
Magnesium | 0.47 | percent by weight | AES_HF |
Aluminum | 7.7 | percent by weight | AES_HF |
Phosphorus | 0.09 | percent by weight | AES_HF |
Potassium | 2.1 | percent by weight | AES_HF |
Calcium | 0.38 | percent by weight | AES_HF |
Scandium | 18 | parts per million by weight | AES_HF |
Titanium | 0.34 | percent by weight | AES_HF |
Vanadium | 200 | parts per million by weight | AES_HF |
Chromium | 130 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.6 | percent by weight | AES_HF |
Cobalt | 21 | parts per million by weight | AES_HF |
Nickel | 76 | parts per million by weight | AES_HF |
Copper | 67 | parts per million by weight | AES_HF |
Zinc | 120 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 730 | parts per million by weight | AES_HF |
Strontium | 120 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 13 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L5 | parts per million by weight | AES_HF |
Barium | 1200 | parts per million by weight | AES_HF |
Lanthanum | 23 | parts per million by weight | AES_HF |
Cerium | 42 | parts per million by weight | AES_HF |
Neodymium | 24 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Mercury | 140 | parts per million by weight | AA_CV |
Lead | 15 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |